A new investment material for the pressing loss wax technique for dental glass ceramics. It has been found that the addition of fillers to a magnesium phosphate investment, specifically metal oxides with elevated melting points ranging from 1800 to 2800.degree. C., provides a protection barrier against the reaction between the high alkaline content of the glass ceramic and the investment during the pressing process in the range of 800 to 950.degree. C. Specifically, it has been found that the addition of aluminum oxide of about 2 to 5 percent of the total dry mix in combination with any of the zirconium oxide, yttrium stabilized zirconium, titanium dioxide and boron nitride in proportions of about 3.5%, enhances the barrier against a surface reaction and improves the thermal properties of the investment.